Silicon (Si), NIST 640c

a = 0.54311946 ± 0.00000092 nm at 22.5 °C

Lanthanum Hexaboride (LaB6), NIST 660a

a = 0.41569162 nm ± 0.00000097 nm at 22.5 °C